发表刊物：ChemElectroChem

项目来源：国家自然科学基金项目

关键字：metal-organic framework; silica spheres; cobalt oxide; nitrogen-doped carbon; glucose sensors

摘要：As glucose molecules are well recognized to supplement the main energy source of living cells as the intermediate product of metabolism in human body, it is of great importance to develop a convenient and quantitative glucose sensor with high selectivity, high sensitivity, and high accuracy. In this work, a simple and novel strategy has been developed to obtain a high‐performance non‐enzymatic glucose sensor by constructing hierarchically porous Co3O4 embedded into the metal organic framework (MOF)‐derived N‐doped carbon matrix based on a SiO2 template, denoted as ST‐Co3O4. The removal of the SiO2 template creates abundant voids and a large specific surface for the obtained layered mesoporous ST‐Co3O4 composite, which enhances the electron transfer kinetics and the ability to adsorb biomolecules, further greatly improving the surface reaction efficiency and promoting the improvement of its catalytic performance. Compared with pure Co3O4 nanoparticles from ZIF‐67 without a silica template, as‐obtained ST‐Co3O4 shows a good mesoporous environment, provides more active sites, and makes the non‐enzymatic glucose sensor exhibit high sensitivity (2860&#8197;μA mM&#8722;1&#8201;cm&#8722;2) and fast response time (<1&#8197;s) over a wide linear glucose concentration range of 1.0–1300.0&#8197;μM. Additionally, the ST‐Co3O4/CC electrode demonstrates good anti‐interference, high repeatability, and robust stability (>3000&#8197;s), which can repeatedly detect the glucose species in real human serum (RSD<9.69&#8201;%, n=3), and shows broad prospects in non‐enzymatic sensors.

第一作者：钱金杰

通讯作者：钱金杰,胡悦

卷号：5

ISSN号：2196-0216

是否译文：否

CN号：10.1002/celc.202001588

发表时间：2021-01-20